Hysol®Huawei KL1000-3NP™ epoxy molding compounddelivers outstanding performance and ease of use
.Huawei KL1000-3NP™ meets UL 94 V-0 Flammability at3.175mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 20Spiral Flow, @ 175°C, cm 75Shelf Life:@ 5oC, months 12TYPICAL PROCESS DATAHandling
Preheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time:Conventional mold, seconds 10 to 18Automold, seconds 4 to 10Curing Time, @ 175oC:Conventional mold, seconds 40 to 100Automold, seconds 40 to 80Post Cure @ 175°C, hours 4 to 6Huawei KL1000-3NP™ has been formulated to provide the bestpossible moldability and as wide a molding latitude as possible.Although molding and curing conditions will vary from situation to ituation, recommended starting ranges are shown above.TYPICAL PROPERTIES OF CURED MATERIALAll measurements taken at 25 °C unless otherwise noted.
All physical,electrical and analytical measurements taken on specimens curedfor 2 minutes @ 175 °C with post cure of 6 hours at 175 °C, unlessother wise specified
Hysol®HuoliKL1000-3NP™环氧树脂成型复合材料具有出色的性能和易用性.Huawei KL1000-3NP™符合UL 94 V-0可燃性，厚度为3.7575mm。
固化材料的典型特性时间@ 175°C秒秒20螺旋流@ @ 175℃，厘米75Shelf寿命：@ 5℃，月12工艺流程数据处理预热温度：常规模具，°C 80至100Automold，秒0至5模具温度，℃150至195压铸压力，Kg /cm240至100转印时间：常规模具秒10至18Auold，秒4至10℃，@ 175℃：常规模具，秒40至100Automold，秒40至80后固化175℃，小时4至6Huawei KL1000-3NP™已经配制，以提供尽可能*佳的可模塑性和宽的成型纬度。
尽管成型和固化条件将变化从情况到情况，推荐的启动范围如上所示。
固化材料的特性所有测量在25°C下进行，除非另有说明。
所有物理，电学和分析测量在175℃下固化2分钟，175℃下固化6小时，除非另有规定 |