汉高汉高乐泰乐泰 Tra-bond F 112
技术服务热线：021-51693135 / 021-22818476
TRA-BOND F112 adhesive is formulated for fiber optic assembly applications.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Thixotropic Index 1.0
Viscosity @ 25 °C, mPa∙s (cP):
After Mixing 1,800
Specific Gravity, cured 1.2
Pot Life:
@ 2grams, minutes 30
Work Life:
@ 2grams, hour 1
Flash Point - See MSDS
TYPICAL CURING PERFORMANCE
Cure Schedule
24 hours @ 25°C or
1 hour @ 65°C or
15 minutes @ 90°C
Sufficient cure in 15 minutes @ 65oC is developed for polishing connectors.
The above cure profiles are guideline recommendations. Cure conditions (time and temperature) may vary based on customers' experience and their application requirements, as well as customer curing equipment, oven loading and actual oven temperatures.
TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties:
Coefficient of Thermal Expansion, cm/cm/oC 6.20×10+01
Glass Transition Temperature (Tg), ultimate, °C 102
Hardness, Shore D 86
Refractive Index 1.51
Water Absorption , after 24 hours saturation, % 0.07
tra-bond F112胶光纤装配应用制定。
固化材料的典型性能
触变指数1
粘度@ 25°C，MPA∙S（CP）：
混合后的1800
比重，固化1.2
锅里的生活：
“2grams，30分钟
工作生活：
“2grams，小时1
闪光点看到MSDS
典型的固化性能
治疗计划
24小时@ 25°C或
1小时@ 65°C或
15分钟@ 90°C
15分钟@ 65oC足疗用于抛光的连接器。
上述固化型材指南建议。固化条件（时间和温度）可能会根据客户的经验和他们的应用要求，以及客户固化设备，烘箱负荷和实际烤箱温度变化。
固化材料的典型性能
物理性质：
热膨胀系数，厘米/厘米/oC 6.20×10 + 01
玻璃化转变温度（Tg），极限，°C 102
硬度，岸上D 86
折射率1.51
吸水，24小时饱和度后，% 0.0 |