乐泰® AA 3108™ is designed primarily for potting and sealing glass to metal joints that must withstand thermal cycling and environmental exposure. The product has shown excellent capabilities in bonding dissimilar rigid substrates.
TYPICAL PROPERTIES OF UNCURED MATERIAL Specific Gravity @ 25 °C 1.08Flash Point - See SDS Viscosity, Brookfield - RVT, 25 °C, mPa•s (cP):Spindle 4, speed 20 rpm, 3,600 to 6,600LMSTYPICAL CURING PERFORMANCE乐泰® AA 3108™ can be cured by exposure to UV light at365 nm.
Surface cure is enhanced by exposure to UV light in the 220 to 260 nm range. Cure rate and ultimate depth of cure depend on light intensity, spectral distribution of the light source, exposure time and light transmittance of the substrate through which the light must pass. Fixture Time Fixture time is defined as the time to develop a shear strength of 0.1 N/mm2.UV Fixture Time, Glass, seconds: Medium Pressure Hg Arc bulb, Zeta®7200 light source:50 mW/cm2, measured @ 365 nm ≤15LMSElectrodeless, D bulb:100 mW/cm2, measured @ 365 nm 7StorageStore product in the unopened container in a dry location.
Storage information may be indicated on the product containerlabeling.
Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or greater than 8 °C can adversely affect product properties.
乐泰®AA 3108™主要用于盆栽和密封玻璃与金属接头，必须承受热循环和环境暴露。该产品在粘合不相似的刚性基材中显示出优异的性能。
固化材料的特性特性25℃下的特定重力1.08闪点 - 参见SDS
粘度，Brookfield - RVT，25°C，mPa•s（cP）：主轴4，转速20 rpm，3,600至6,600LMS特殊固化性能AA 3108™可通过暴露于365 nm的紫外线固化。通过暴露在220至260nm范围内的紫外线来增强表面固化。固化速率和*极深度取决于光强度，光源的光谱分布，光线必须通过的穿透线的曝光时间和透光率。混合时间混合时间定义为开发剪切强度为0.1 N /mm2的时间.UV夹具时间，玻璃，秒：中压Hg电弧灯泡，Zeta®7200光源：在365nm下测量的50mW / cm 2≤15LMS无电极，D灯泡：100mW / cm 2，在365nm下测量7StorageStore产品在未打开 |
 |
|
|