HYSOL KL1000-3LX电子胶水/塑封胶水/汉高乐泰胶水/塑封方案
技术服务热线：021-51693135 / 021-22818476
乐泰 HYSOL KL 1000-3LXP provides the lowest cost ofownership with superior moldability and reliability.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 27Spiral Flow, @ 175°C, inch 33Shelf Life @ 5oC, months 12Specific Gravity 2.04TYPICAL PROCESS DATAHandlingPreheat Temperature , °C 80 to 90Molding Temperature, °C 170 to 190Transfer Pressure, Kgf/cm2 40 to 85Transfer Time, seconds 5 to 10Curing Time, 3 mm section:@ 175oC 50 to 90乐泰 HYSOL KL 1000-3LXP has been formulated to provide thebest possible moldability and as wide a molding latitude as possible.Although molding and curing conditions will vary from situation tosituation, recommended starting ranges are shown above.
TYPICAL PROPERTIES OF CURED MATERIALAll measurements taken at 25 °C unless otherwise noted.
All physical,electrical and analytical measurements taken on specimens curedfor 2 minutes @ 175 °C with post cure of 6 hours at 175 °C, unlessother wise specified
乐泰 HYSOL KL 1000-3LXP提供*低的拥有成本，具有优异的成型性和可靠性。
固化材料的特性特性时间@ 175°C秒秒27螺旋流@ 175°C，英寸33Shelf寿命@5oC，月12特殊重力2.04特殊工艺数据处理预热温度，°C 80至90模具温度，°C 170至190转印压力，Kgf /cm240至85转印时间，秒5至10℃，3 mm截面：@175oC50至90LOCTI HYSOL KL 1000-3LXP已配制成*佳可能的成型性和尽可能宽的成型纬度。
尽管成型和固化条件将根据不同情况而有所不同，但推荐的起始范围如上所示。固化材料的特性除非另有说明，否则在25°C下进行所有测量。
所有物理，电学和分析测量在175℃下固化2分钟，175℃下固化6小时， |
 |
|
|