乐泰 HYSOL GR 2720 is a green epoxy based moldingcompound designed for the encapsulation of passivecomponents.
This material is an excellent candidate for the
molding of pressure sensitive components.乐泰 HYSOL GR 2720 meets UL 94 V-0 Flammability at6.35mm thickness.TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 19Spiral Flow, @ 175°C, inches 38Shelf Life:@ -18oC, months 6
Hot Hardness,Shore-D@ 175°C, 90 seconds 90TYPICAL PROCESS DATAHandling
Preheat Temperature , °C 80 to 95Molding Temperature, °C 140 to 180Transfer Pressure, Kgf/cm2 40 to 85Transfer Time, seconds 6 to 15Curing Time, 3 mm section:Conventional mold:@ 175oC, seconds 70 to 90Automold:@ 175oC, seconds 50 to 70Post Cure @ 175°C, hours 2 to 6StorageStore product in the unopened container in a dry location.
Storage information may be indicated on the product containerlabeling.Powder Storage - Powder or preforms should be stored at -4oCor below, in closed containers.
After removal from cold torage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination.
The suggested waiting time for a standard 15kg carton box is 24 hours.
乐泰 HYSOL GR 2720是一种绿色环氧基成型复合材料，专为封装被动元件而设计。
这种材料是很好的候选人压力敏感部件的成型.
乐泰 HYSOL GR 2720符合UL 94 V-0可燃性，厚度为6.355mm。固化材料的特性固体时间@ 175°C，秒19螺旋流，@ 175°C，英寸38Shelf寿命：@-18oC，月6热硬度，Shore-D @ 175°C，90秒90工艺流程数据处理预热温度°C 80至95模具温度°C 140至180转印压力Kgf /cm240至85转印时间秒6至15烘烤时间3毫米截面：常规模具：@ 175℃，秒70至90Automold：@ 175℃，秒50至70次固化@ 175°C，小时2至6个储存在未开封的容器中的产品在干燥的位置。
储存信息可能在产品容器标签上显示。
粉末储存 - 粉末或预型件应储存在-4oC以下，密闭容器。
从寒冷除去后储存时，必须在密封容器中允许材料进入室温，以避免水分污染。
建议的等待时间为标准15kg纸箱是24小时。 |
 |
|
|