乐泰 HYSOL GR 2710 epoxy molding compound deliversoutstanding performance and ease of use.
乐泰 HYSOL GR 2710 meets UL 94 V-0 Flammability at6.35mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 15Spiral Flow, @ 177°C, cm 88.9Shelf Life:@ 5oC, days 365Hot Hardness,Shore-D@ 175°C, 90 seconds 85TYPICAL PROCESS DATAHandlingPreheat Temperature , °C 80 to 95Molding Temperature, °C 140 to 180Transfer Pressure, Kgf/cm2 40 to 85Transfer Time, seconds 6 to 15Curing Time, :@ 177oC, seconds 45 to 60Curing Time, 3 mm
section:Conventional mold:@ 175oC, seconds 70 to 90Automold:@ 175oC, seconds 50 to 70Post Cure @ 175°C, hours 2 to 6StorageStore product in the unopened container in a dry location.
Storage information may be indicated on the product containerlabeling.Powder Storage - Powder or preforms should be stored at 10oC or below, in closed containers.
After removal from cold
storage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination.
The suggested waiting time for a standard 15kg carton box is 24 hours.
乐泰 HYSOL GR 2710环氧树脂模塑料具有出色的性能和易用性.
乐泰 HYSOL GR 2710符合UL 94 V-0可燃性，厚度为6.355mm。固化材料的典型特性时间@ 175°C秒秒15螺旋流量，@ 177°C，cm 88.9Shelf寿命：@5oC，365天硬度，Shore-D @ 175°C，90秒85特殊工艺数据处理预热温度，°C 80至95模压温度，°C 140至180转印压力Kgf /cm240至85转印时间秒6至15凝固时间：177℃，秒45至60℃烘烤时间3毫米截面：常规模具：@ 175℃，秒70至90Automold： @175oC，秒50至70后固化@ 175°C，小时2至6储存在未开封容器中的产品在干燥的位置。
储存信息可能在产品容器标签上指示。粉末储存 - 粉末或预制件应存放在10oC或更低，在封闭的容器中。从寒冷除去后
储存时，必须在密封容器中允许材料进入室温，以避免水分污染。
建议的等待时间为标准15kg纸箱是24小时。 |
 |
|
|