Teroson EP 1450
TEROSON EP 1450 is an expanding one component, high strength structural foam based on Epoxy. The non cured material is resistant to washing and phosphating solutions in normal use in automotive industry and to electro dip painting. The final part gets its geometric shape i.e. by injection molding. TEROSON EP 1450 will cure while passing the EC-oven.
APPLICATION AREAS
TEROSON EP 1450 must be applied as a preformed part in the body shop. The material increases stiffness, strength, fatigue limits and vibration behavior of vehicle bodies. The part is clipped into hollow cavities.
TECHNICAL DATA
(Typical Test Results)
Uncured
Colour grey
Consistency solid
Density at delivery approx. 1.3 g/cm3
Solids Content
(3 h, 105 °C)
> 99 %
Cured
Recommended curing conditions:
mini: 15 min 155°C (keep)
maxi: 20 min 195°C (keep)
Density after expansion approx. 0.6 g/cm3
Expansion > 100 %
Compression test
Compressive strength > 10 MPa
Compressive modulus > 450 MPa
Lap shear strength
Substrates galvanized steel
Bonding area 20 x 25 mm
Layer thickness 2 mm
Strength > 2 MPa
Glass transition
temperature range
(Tg) DMTA (40 Hz, 2 K/min)
> 100 °C
Corrosion resistance
Salt spray test
(35 °C, salt solution 5 %,
500 hours)
no corrosion, no loss of adhesion
Corrosion test (VDA 621-415) no corrosion, no loss of adhesion
Water absorption
(24 h, 98 % humidity, 40 °C)
< 0.5 % weight increase
In service temperature -30 to 80 °C
泰罗松EP 1450是一个扩展的一个组成部分，基于环氧树脂高强度结构泡沫。非固化材料对汽车行业的清洗和磷化液具有良好的耐腐蚀性，可用于电涂漆。*后一部分得到其几何形状，即注塑成型。泰罗松EP 1450治愈而通过EC炉。
应用领域
泰罗松EP 1450作为预留部分美体小铺。该材料增加刚度，强度，疲劳极限和振动行为的车身。该部件被夹在空心空腔中。
技术数据
（典型测试结果）
未固化的
颜色灰色
一致性固体
密度约1.3克/厘米3交货